Product Details:
|
| Thermal Conductivi: | 0.17 | Package: | Braided Bag/carton |
|---|---|---|---|
| Tempreture: | 1260 | Type: | Ceramic Raw Materials |
| Temprature Classification: | 1260℃-1600℃ | Fire Resistance: | Non-combustible |
| Raw Material: | Aluminosilicate | Size: | 600mmX400mmX(10-50)mm Or Customized |
| Length: | 7200 Mm | Apparent Porosity: | 18 |
| Use: | Insulation | Moisture Content: | ≤1% |
| Service Temperature: | 1000-1300 Degree | Application: | Insulation And Fire Protection |
| Width: | 610 Mm | ||
| Highlight: | Kiln Oven Thermal Insulation Material,Aluminum Silicate Fiber Blanket,1260 Ceramic Fiber Blanket |
||
Kiln oven thermal insulation material 1260 ceramic fiber blanket 128kg/m3 160kg/m3 aluminum silicate fiber blanket
Ceramic Fiber Blanket Introduce
Ceramic Fiber Blanket is composed of long flexible, interwoven fibers manufactured by the “spun” process yielding a strong,lightweight, durable product. This material can be used for applications with temperatures from 1000°F (538°C) to 2600°F (1425°C).The product is firm, light and durable.Thermal and physical properties are retained after drying following wetting by oil, steam or water. This ceramic fiber blanket products are completely inorganic, so there are no fumes when heating for the first time.Rongsheng ceramic fiber blanket has higher tensile strength and longer service life.
Production Advantages:
1. Excellent thermal stability,low heat storage,low shrinkage,low thermal conductivity
2. Good obstructing voice and mechanism streng
3. Good springiness for fibers,resistance to thermal shock
Typical Application:
1.Industrial furnace, heating devices, high temperature pipe wall linings,high temperature filter materials
2.High tempeture boilers, steam turbine and Nuclear power thermal insulation
3.Chemical industrial high-temperature reaction equipment and heating equipment wall linings
4.High building fireproof and thermal insulation,furnace door and roof thermal insulation
Ceramic Fiber Insulation Blanket Specification
| Type | 1260 Blanket | 1400 Blanket | 1500 Blanket | 1600 Blanket |
| Classification temperature ( °C) | 1260 | 1425 | 1500 | 1600 |
| Melting point (°C) | 1760 | 1700 | 1760 | - |
| Colour | White | White | Blue gree | White |
| Fiber diameter ( u m) | 2.6 | 2.8 | 2.65 | 3.1 |
| Fiber length (mm) | ~250 | ~250 | ~150 | ~100 |
| Linear shrinkage(%) | (1100oC x 24 hrs)1.8 | (1300 o C x 24 hrs) 1.5 | - | - |
| Shot content (>212 micro meter) (%) | 18 | 18 | - | - |
| Thermal conductivity Kcal/mh °C (W/mK) ,ASTM C201 | ||||
| 1260 blanket | 64 kg/m3 | 96 kg/m3 | 128 kg/m3 | 160kg/m3 |
| mean 400°C | 0.13 | 0.12 | 0.07 | 0.09 |
| mean 600 °C | 0.21 | 0.17 | 0.12 | 0.14 |
| mean 800°C | 0.30 | 0.25 | 0.16 | 0.20 |
| 1400 blanket | - | - | 128 kg/m3 | 160kg/m3 |
| mean 600 °C | - | - | 0.13 | 0.14 |
| mean 800 °C | - | - | 0.20 | 0.20 |
| mean1000 °C | - | - | 0.29 | 0.28 |
| Chemical composition (%) | ||||
| 1260 Blanket | 1400 Blanket | 1500 Blanket | 1600 Blanket | |
| Al2O3 | 47.1 | 35.0 | 40.0 | 72 |
| SiO2 | 52.3 | 49.7 | 58.1 | 28 |
| ZrO2 | - | 15.0 | - | - |
| Cr2O3 | - | - | 1.8 | - |
| Bulk density(Kg/m3) | 64,96,128,160 | |||
| Available size(mm/roll) | 7200*600*6,12.5,20,25,38;3600*600*50 | |||
Standard ceramic fiber blanket - working temperature 1050 ℃
High-alumina ceramic fiber blanket - working temperature 1260 ℃
Zirconia ceramic fiber blanket - working temperature 1350 ℃
Bulk density:64 kg/m3,96 kg/m3,128 kg/m3,160kg/m3