Product Details:
|
| Place Of Origin:: | Henan, China | Shape:: | Brick |
|---|---|---|---|
| Material:: | MgO-Carbon Brick, MgO-Carbon Brick | SiO2 Content (%):: | Little |
| Al2O3 Content (%):: | 60-75% | MgO Content (%):: | 8-12%, ≥70% |
| CaO Content (%):: | 0.34% | Refractoriness (Degree ): | Ee): 1770°< Refractoriness< 2000°, 1770°< Refractoriness< 2000° |
| CrO Content (%):: | 0.002% | SiC Content (%):: | 1.2-1.4 |
| Model Number:: | Magnesia Carbon Brick | Brand Name:: | Rongsheng |
| Bulk Density/ G/cm3:: | ≥2.77 | Feature:: | Great Performance To Anti-slag |
| Highlight: | Mg-C Bricks For Eafs Furnace,Refractory Andalusite Magnesia Carbon Brick,Magnesia Carbon Refractory Bricks for Furnace |
||
Quick Detail:
Al2O3-MgO-C Brick For Refining Ladle has low porosity ratio,good corrosion resistance,watering resistance,spalling resistance.
Description:
Alumina silicon carbide carbon brick using grade alumina, fused alumina, silicon carbide, graphite and high-pressure molding of additives, mainly for ordinary ladle, ladle desulfurization, Large torpedo car.
Alumina silicon carbide carbon brick as a composite refractories, Effective use of the high thermal capacity and strong resistance to slag erosion and magnesia carbon, low expansion, the biggest drawback is compensated magnesia poor chipping resistance.
Specifications:
|
Al2O3-SiC-C Brick
|
ASC-Z | ASC-R |
| Al2O3(%) ≥ | 63 | 65 |
| SiC (%) ≥ | 12 | 9 |
| C (%) ≥ | 10 | 5 |
| Apparent Porosity ≤ | 7 | 8 |
| Bulk Density (g/cm3)≥ | 2.90 | 2.92 |
| C.C.S(MPa)≥ | 50 | 50 |
| R.U.L in 0.2MPa | 1650 | 1650 |
| Application | Slag lining | Side wall, bottom |